Rilsan® BESHV BLK T is an ultra high viscosity Polyamide 11 grade specifically designed to be

extruded into large diameter thick wall pipe. This grade has been specifically engineered to ac

hieve an outstanding balance of properties for Oil & Gas piping applications. It offers a cost eff

ective system for non-metallic corrosion free fluid transfer in critical Oil and Gas industry appli

cations. Rilsan® Polyamide 11 is the only thermoplastic material permitted by the US Departm

ent of Transportation (DOT) under the Code of Federal Regulations (CFR) Title 49, Part 192, for

gas distribution piping to be installed and operated at pressures up to and including 200 psi in

a design factor of 0.40

MAIN APPLICATIONS

• Oil & Gas piping applications.

• 基本信息
  特性	可更新资源 粘度，高
  用途	管道系统
  加工方法	挤出

  物理性能	额定值	单位制	测试方法
  密度	1.03	g/cm³	ISO 1183

  硬度	额定值	单位制	测试方法
  肖氏硬度			ISO 868
  邵氏 D	77		ISO 868
  邵氏 D, 15 秒	72		ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸模量	1390	MPa	ISO 527-2
  拉伸应力			ISO 527-2
  屈服	42.0	MPa	ISO 527-2
  断裂	52.0	MPa	ISO 527-2
  拉伸应变			ISO 527-2
  屈服	5.0	%	ISO 527-2
  断裂	> 200	%	ISO 527-2
  弯曲模量	1180	MPa	ISO 178

  冲击性能	额定值	单位制	测试方法
  简支梁缺口冲击强度			ISO 179
  -30°C	11	kJ/m²	ISO 179
  23°C	10	kJ/m²	ISO 179
  简支梁无缺口冲击强度			ISO 179
  -30°C	无断裂		ISO 179
  23°C	无断裂		ISO 179

  热性能	额定值	单位制	测试方法
  熔融温度	189	°C	ISO 11357-3

  补充信息	额定值	单位制	测试方法
  ASTM Classification	PA0320 B32300		ASTM D4066
  Renewable Carbon Conent	> 95	%	ASTM D6866

  注射	额定值	单位制
  干燥温度	176	°C
  干燥时间	12	hr
  加工（熔体）温度	240 到 290	°C
  模具温度	20.0 到 60.0	°C