ARLEN™ E630N by Mitsui Chemicals is a modified polyamide 6T reinforced with 30% glass fiber. Possesses high dimensional stability, high melting point, high rigidity and minimum water absorption. Exhibits good chemical and heat resistance. Is suitable for processing by injection molding. ARLEN™ E630N is recommended for electrical & electronic parts including connectors, jacks, switches and power supply terminals. Complies with UL 94 V-0 flame rating.

Features:

• High dimensional stability

• High melting point

• High rigidity

• Minimum water absorption

• Good chemical and heat resistance

• Flame retardant

Applications:

• Electrical and electronic parts including: connectors, jacks, switches, and power supply terminals.
• ARLEN™ E630N 物性表

  基本信息
  填料/增强材料	玻璃纤维增强材料, 30% 填料按重量
  添加剂	阻燃性
  特性	Good Heat Resistance High Dimensional Stability 刚性，高 耐化学性良好 吸水低或不吸水 阻燃性
  用途	电气/电子应用领域 开关 连接器
  加工方法	注射成型

  物理性能	额定值	单位制	测试方法
  比重	1.58	g/cm³	ASTM D792
  收缩率			ASTM D955
  流动	0.20	%	ASTM D955
  横向流动	0.80	%	ASTM D955
  吸水率 (23°C, 24 hr, 65%r.h)	2.1	%	ASTM D570

  硬度	额定值	单位制	测试方法
  洛氏硬度 (M 级)	100		ASTM D785

  机械性能	额定值	单位制	测试方法
  抗张强度	210	MPa	ASTM D638
  伸长率 (断裂)	6.0	%	ASTM D638
  弯曲模量	12500	MPa	ASTM D790
  弯曲强度	275	MPa	ASTM D790

  冲击性能	额定值	单位制	测试方法
  悬壁梁缺口冲击强度	100	J/m	ASTM D256

  热性能	额定值	单位制	测试方法
  载荷下热变形温度 (1.8 MPa, 未退火)	310	°C	ASTM D648
  玻璃转化温度	95.0	°C
  熔融温度	320	°C
  线形热膨胀系数			ASTM E831
  流动	1.6E-5	cm/cm/°C	ASTM E831
  横向	6.8E-5	cm/cm/°C	ASTM E831

  电气性能	额定值	单位制	测试方法
  体积电阻率	1.0E+15	ohms·cm	ASTM D257
  介电强度	24	kV/mm	ASTM D149
  介电常数 (1 MHz)	3.90		ASTM D150
  耗散因数 (1 MHz)	0.013		ASTM D150

  可燃性	额定值	单位制	测试方法
  UL 阻燃等级	V-0		UL 94