EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their use as bases for all-purpose concentrates for addition to a wide spectrum of polymers. They process like LDPE.

基本信息
特性	低温韧性 高 ESCR（抗应力开裂） 共聚物 韧性良好 柔软
用途	薄膜 管件 医疗/护理用品 粘结树脂
机构评级	FDA 21 CFR 177.1340
形式	粒子
加工方法	薄膜挤出

物理性能	额定值	单位制	测试方法
密度	0.946	g/cm³	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	0.70	g/10 min	ASTM D1238
甲基丙烯酸含量	20.5	wt%

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)	35		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度 1(断裂)	14.0	MPa	ASTM D638
伸长率 2(断裂)	790	%	ASTM D638

薄膜	额定值	单位制	测试方法
割线模量			ASTM D882
1% 正割, MD : 38 µm, 吹塑薄膜	52.0	MPa	ASTM D882
1% 正割, TD : 38 µm, 吹塑薄膜	49.0	MPa	ASTM D882
抗张强度			ASTM D882
MD : 断裂, 38 µm, 吹塑薄膜	23.0	MPa	ASTM D882
TD : 断裂, 38 µm, 吹塑薄膜	17.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 µm, 吹塑薄膜	420	%	ASTM D882
TD : 断裂, 38 µm, 吹塑薄膜	680	%	ASTM D882
落锤冲击 (38 µm, 吹塑薄膜)	360	g	ASTM D1709A
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 µm, 吹塑薄膜	46	g	ASTM D1922
TD : 38 µm, 吹塑薄膜	290	g	ASTM D1922
始封温度	67.0	°C

热性能	额定值	单位制	测试方法
脆化温度	< -73.0	°C	ASTM D746
维卡软化温度	54.0	°C	ASTM D1525
熔融峰值温度	79.0	°C	ASTM D3418

光学性能	额定值	单位制	测试方法
光泽度 (45°, 38.1 µm, 吹塑薄膜)	22		ASTM D2457
雾度 (38.1 µm, 吹塑薄膜)	30	%	ASTM D1003