PES film possesses a combination of properties such as high resistance to heat and combu

stibility, low smoke emission and transparency. These coupled with light weight, high tear i

nitiation and propagation strength, dimensional stability, chemical resistance and thermofo

rmability make the film particularly useful in electrical, aerospace, automotive, and mass tra

sit industries.

Applications Include:

• Liquid crystal displays

• Radomes

• Magnet wire insulation

• Hot melt adhesives

• Flex circuitry

• High temperature labels

• High heat deflection and continuous use temperature

• Exceptional tensile and flexural strength

• High dielectric strength

• Exceptional mechanical properties

• Dimensionally stable at varying temperatures

• Transparency

• Hydrolytically stable

• 基本信息
  特性	尺寸稳定性良好 低烟度 高拉伸强度 激光标记 抗燃 良好的撕裂强度 耐化学性良好 耐热性，高 水解稳定
  用途	LCD 应用 薄膜 标签 电气/电子应用领域 航空航天应用 浸渍类用途 汽车领域的应用 粘合剂
  外观	清晰/透明
  形式	薄膜
  加工方法	热成型

  物理性能	额定值	单位制	测试方法
  比重	1.37	g/cm³	ASTM D792
  吸水率 (24 hr)	0.70	%	ASTM D570

  薄膜	额定值	单位制	测试方法
  抗张强度 - MD (屈服)	72.4	MPa	ASTM D882
  伸长率 - MD (断裂)	52	%	ASTM D882
  弯曲模量 - MD	2550	MPa	ASTM D790
  面积系数	20000	in²/lb/mil

  补充信息	额定值	单位制	测试方法
  Tear Strength - prop	37.1	kN/m	ASTM D1004
  Thermoforming Molding Temperature	270 到 280	°C

  热性能	额定值	单位制	测试方法
  载荷下热变形温度 (1.8 MPa, 未退火)	195	°C	ASTM D648
  连续使用温度	180	°C
  玻璃转化温度	225	°C	ASTM D3418

  电气性能	额定值	单位制	测试方法
  表面电阻率	> 1.0E+14	ohms	ASTM D257
  介电强度 (0.102 mm)	180	kV/mm	ASTM D149
  介电常数 (1 kHz)	3.50		ASTM D150
  耗散因数 (1 kHz)	0.011		ASTM D150

  可燃性	额定值	单位制	测试方法
  极限氧指数	38	%	ASTM D2863

  光学性能	额定值	单位制
  折射率	1.650
  透射率	91.0	%