牌号
|
|
|||
|
材料供应商
|
|
|||
|
搜索 UL 黄卡
|
|
|||
|
供货地区
|
|
|||
|
性能特点
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
1.27
|
g/cm³
|
ASTM D792, ASTM D1505 |
|
23°C
|
1.27
|
g/cm³
|
ISO 1183/D |
|
吸水率 (23°C, 24 hr)
|
0.13
|
%
|
ASTM D570, ISO 62 |
|
固有粘度 2
|
Internal Method | ||
|
Film : 23°C
|
0.70
|
|
|
|
Pellets : 23°C
|
0.75
|
|
|
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
R 计秤, 23°C
|
106
|
|
ASTM D785 |
|
R 计秤, 23°C
|
109
|
|
ISO 2039-2 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 (23°C)
|
2100
|
MPa
|
ASTM D638, ISO 527-2 |
|
抗张强度
|
ASTM D638, ISO 527-2 | ||
|
屈服, 23°C
|
50.0
|
MPa
|
|
|
断裂, 23°C
|
28.0
|
MPa
|
|
|
伸长率
|
|||
|
断裂, 23°C
|
130
|
%
|
ASTM D638 |
|
断裂, 23°C
|
100
|
%
|
ISO 527-2 |
|
弯曲模量
|
|||
|
23°C
|
2100
|
MPa
|
ASTM D790 |
|
23°C
|
2000
|
MPa
|
ISO 178 |
|
弯曲强度
|
|||
|
23°C
|
68.0
|
MPa
|
ISO 178 |
|
屈服, 23°C
|
70.0
|
MPa
|
ASTM D790 |
|
撕裂阻力
|
ASTM D2582 | ||
|
M.D. : 23°C
|
93
|
N
|
|
|
T.D. : 23°C
|
93
|
N
|
|
| 薄膜 |
额定值
|
单位制
|
测试方法
|
|
薄膜厚度 - 经测试
|
250
|
µm
|
|
|
割线模量
|
ASTM D882 | ||
|
MD
|
1900
|
MPa
|
|
|
TD
|
1900
|
MPa
|
|
|
抗张强度
|
ASTM D882 | ||
|
MD : 屈服
|
52.0
|
MPa
|
|
|
TD : 屈服
|
52.0
|
MPa
|
|
|
MD : 断裂
|
59.0
|
MPa
|
|
|
TD : 断裂
|
55.0
|
MPa
|
|
|
伸长率
|
ASTM D882 | ||
|
MD : 屈服
|
4.0
|
%
|
|
|
TD : 屈服
|
4.0
|
%
|
|
|
MD : 断裂
|
400
|
%
|
|
|
TD : 断裂
|
400
|
%
|
|
|
落锤冲击 3
|
ASTM D1709A | ||
|
-18°C
|
500
|
g
|
|
|
23°C
|
400
|
g
|
|
|
埃尔曼多夫抗撕强度
|
ASTM D1922 | ||
|
MD
|
1400
|
g
|
|
|
TD
|
1700
|
g
|
|
|
裤型撕裂耐性 4
|
ISO 6383-1 | ||
|
MD
|
36.0
|
N/mm
|
|
|
TD
|
36.0
|
N/mm
|
|
|
透氧率 (23°C)
|
10
|
cm³·mm/m²/atm/24 hr
|
ASTM D3985 |
|
水气透过率 (38°C, 100% RH)
|
7.0
|
g/m²/24 hr
|
ASTM F1249 |
|
Carbon Dioxide Permeability 5 (23°C)
|
49
|
cm³·mm/m²/atm/24 hr
|
ASTM D1434 |
|
Tear Propagation Resistance 6
|
ASTM D1938 | ||
|
M.D. : 23°C
|
36
|
kN/m
|
|
|
T.D. : 23°C
|
36
|
kN/m
|
|
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
|||
|
-40°C
|
37
|
J/m
|
ASTM D256 |
|
23°C
|
100
|
J/m
|
ASTM D256 |
|
-40°C
|
4.2
|
kJ/m²
|
ISO 180/1A |
|
23°C
|
6.2
|
kJ/m²
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|||
|
-40°C, 3.20 mm
|
无断裂
|
|
ASTM D4812 |
|
-30°C, 3.20 mm
|
无断裂
|
|
ASTM D4812 |
|
-20°C, 3.20 mm
|
无断裂
|
|
ASTM D4812 |
|
23°C, 3.20 mm
|
无断裂
|
|
ASTM D4812 |
|
-40°C 7
|
无断裂
|
|
ISO 180/1U |
|
-30°C 7
|
无断裂
|
|
ISO 180/1U |
|
-20°C 7
|
无断裂
|
|
ISO 180/1U |
|
23°C 7
|
无断裂
|
|
ISO 180/1U |
|
装有测量仪表的落镖冲击
|
|||
|
-40°C, 2.50 mm, Energy at Peak Load
|
41.0
|
J
|
ASTM D3763 |
|
-40°C, 3.20 mm, Energy at Peak Load
|
50.0
|
J
|
ASTM D3763 |
|
23°C, 2.50 mm, Energy at Peak Load
|
28.0
|
J
|
ASTM D3763 |
|
23°C, 3.20 mm, Energy at Peak Load
|
33.0
|
J
|
ASTM D3763 |
|
-40°C, 2.50 mm, 能量到力量峰值 8, 9
|
35.0
|
J
|
ISO 6603-2 |
|
-40°C, 3.20 mm, 能量到力量峰值 8, 9
|
36.0
|
J
|
ISO 6603-2 |
|
23°C, 2.50 mm, 能量到力量峰值 8, 9
|
40.0
|
J
|
ISO 6603-2 |
|
23°C, 3.20 mm, 能量到力量峰值 8, 9
|
44.0
|
J
|
ISO 6603-2 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
ASTM D648 | ||
|
0.45 MPa, 未退火
|
70.0
|
°C
|
|
|
1.8 MPa, 未退火
|
64.0
|
°C
|
|
|
玻璃转化温度(DSC)
|
80.0
|
°C
|
DSC |
|
维卡软化温度
|
85.0
|
°C
|
ASTM D1525 |
|
线形膨胀系数 - 流动 (-30 到 40°C)
|
0.000051
|
cm/cm/°C
|
ASTM D696 |
|
比热
|
DSC | ||
|
60°C
|
1300
|
J/kg/°C
|
|
|
100°C
|
1760
|
J/kg/°C
|
|
|
150°C
|
1880
|
J/kg/°C
|
|
|
200°C
|
1970
|
J/kg/°C
|
|
|
250°C
|
2050
|
J/kg/°C
|
|
|
导热系数 (23°C)
|
0.21
|
W/m/K
|
ASTM C177 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
1.0E+16
|
ohm
|
ASTM D257 |
|
体积电阻率 (23°C)
|
1.0E+15
|
ohm·cm
|
ASTM D257 |
|
介电强度 10 (23°C)
|
16
|
kV/mm
|
ASTM D149 |
|
介电常数
|
ASTM D150 | ||
|
23°C, 1 kHz
|
2.60
|
|
|
|
23°C, 1 MHz
|
2.40
|
|
|
|
耗散因数
|
ASTM D150 | ||
|
23°C, 1 kHz
|
0.0050
|
|
|
|
23°C, 1 MHz
|
0.020
|
|
|
|
耐电弧性
|
158
|
sec
|
ASTM D495 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
|
光泽度 (45°)
|
108
|
|
ASTM D2457 |
|
透射率
|
ASTM D1003 | ||
|
常规
|
89.0
|
%
|
|
|
总计
|
91.0
|
%
|
|
|
透明度
|
85.0
|
|
ASTM D1746 |
|
雾度
|
0.80
|
%
|
ASTM D1003 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
70.0
|
°C
|
|
|
干燥时间
|
6.0
|
hr
|
|
|
加工（熔体）温度
|
250 到 270
|
°C
|
|
|
模具温度
|
15.0 到 40.0
|
°C
|