Maxiglas® is a continuousl mass polymerization acrylic pellet that has outstanding optical properties, excellent weather resistance, uniform
color and impact resistance. It has exceptional freedom from war page, cracks, scratches, blisters, voids, foreign matter, and other defects
which may affect appearance or serviceability.

Applications:

• Extruded sheets for signage, displays and building material

• Automotive parts such as tail lamps, meter covers and sun visors

• General sundries such as tableware, kitchenware, giftware and bathroom accessories

• Optical lenses such as sunglasses, reading glasses and camera lenses

• Light guide panels for LCD displays
• Maxiglas® MG515 物性表

  基本信息
  特性	光学性能 耐气候影响性能良好
  用途	Automotive Backlights Decorative Displays Displays LCD 应用 Lighting Applications 厨具 光学应用 建筑材料 汽车领域的应用 汽车内部零件 玩具 浴室配件
  形式	粒子
  加工方法	挤出 压缩模塑 注射成型

  物理性能	额定值	单位制	测试方法
  比重	1.19	g/cm³	ASTM D792
  熔流率（熔体流动速率） (230°C/3.8 kg)	15	g/10 min	ASTM D1238
  吸水率 (24 hr)	0.30	%	ASTM D570

  硬度	额定值	单位制	测试方法
  洛氏硬度 (M 级)	90		ASTM D785

  机械性能	额定值	单位制	测试方法
  抗张强度	63.7	MPa	ASTM D638
  伸长率 (断裂)	5.0	%	ASTM D638
  弯曲模量	3140	MPa	ASTM D790
  弯曲强度	93.2	MPa	ASTM D790

  冲击性能	额定值	单位制	测试方法
  无缺口悬臂梁冲击	16	J/m	ASTM D256

  热性能	额定值	单位制	测试方法
  载荷下热变形温度 (1.8 MPa, 未退火)	90.0	°C	ASTM D648
  维卡软化温度	94.0	°C	ASTM D1525

  光学性能	额定值	单位制	测试方法
  折射率	1.490		ASTM D542
  透射率 (3000 µm)	93.0	%	ASTM D1003
  雾度 (3000 µm)	0.30	%	ASTM D1003

  补充信息	额定值	单位制
  Foreign Material 1		mm²

  注射	额定值	单位制
  干燥温度	70.0 到 95.0	°C
  干燥时间	4.0	hr
  料筒后部温度	170 到 210	°C
  料筒中部温度	170 到 210	°C
  料筒前部温度	170 到 210	°C
  模具温度	30.0 到 50.0	°C
  注塑压力	2.76 到 5.52	MPa

  挤出	额定值	单位制
  干燥温度	70.0 到 95.0	°C
  干燥时间	4.0	hr