PPA is a kind of semi-crystalline and semi-aromatic polyamide, it offers high temperature r

esistance, good mechanical properties, oil resistance, low water absorption, good dimensio

nal stability, good processability and it also has good environmental performance. It is rem

arkably stable at high temperature and retains its excellent mechanical and electrical prope

rties in high humidity and chemically aggressive environments.

Applications
Owing to its high performance, there is a wide range of applications of PPA, including under

bonnet automotive components, electronic devices and domestic appliances. Its product cove

rs glass-filled, impact-modified, mineral-filled, high-flow, flame- retardant, high-reflectivity an

d electrical grades.

基本信息
特性	半结晶 尺寸稳定性良好 环保 可加工性，良好 良好的电气性能 耐化学性良好 耐热性，高 耐油性能 吸水低或不吸水
用途	电气/电子应用领域 电器用具 汽车的发动机罩下的零件
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
粘数	70.0 到 90.0	cm³/g	ISO 307
含水量 1		%
灰份含量		%	ISO 3451

热性能	额定值	单位制	测试方法
玻璃转化温度	128 到 138	°C	ISO 11357-2
熔融温度	310 到 320	°C	ISO 11357-3

注射	额定值	单位制
干燥温度	120 到 140	°C
干燥时间	4.0 到 5.0	hr
料筒后部温度	315 到 325	°C
料筒中部温度	320 到 330	°C
料筒前部温度	325 到 335	°C
射嘴温度	325 到 335	°C
模具温度	130 到 140	°C
注塑压力	120	MPa
注射速度	快速
保压	65.0	MPa
螺杆转速	< 150	rpm

挤出	额定值	单位制
干燥温度	120 到 140	°C
干燥时间	4.0 到 5.0	hr
料筒1区温度	250 到 280	°C
料筒2区温度	315 到 340	°C
料筒3区温度	315 到 340	°C
口模温度	300 到 320	°C