聚苯砜Radel R-7159产品说明:
Solvay Specialty Polymers
Radel® R-7159 polyphenylsulfone (PPSU) was developed specifically for aircraft interior applications. The product complies with the FAA regulation 14CFR Part 25 Appendix F, offering vertical burn resistance, very low smoke generation and, through the use of proprietary additives, low heat release values in the Ohio State University (OSU) rate of heat release method. It also generates low flaming-mode toxic gas emissions.
This resin offers good resistance to most fluids found in the aviation industry and is available in a natural color that is designed to accept aircraft paint systems for aesthetic parts. The painting function enhances the chemical resistance of the polymer and provides the final step in color coordination.
Natural: Radel® R-7159 NT 50
美国苏威（聚苯砜）PPSU R-7159物性数据：
美国苏威(聚苯砜)PPSU塑胶原料在中国大陆主要供应商为仁捷塑胶公司，财富热线：18681139818，QQ:13931677，联系人：唐生。
|
特性
|
|
|||
|
用途
|
|
|||
|
机构评级
|
|
|||
|
RoHS 合规性
|
|
|||
|
外观
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.35
|
g/cm³
|
ASTM D792 |
|
熔流率（熔体流动速率） (380°C/2.16 kg)
|
22
|
g/10 min
|
ASTM D1238 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
2280
|
MPa
|
ASTM D638 |
|
抗张强度 (屈服)
|
74.5
|
MPa
|
ASTM D638 |
|
伸长率 (断裂)
|
30 到 50
|
%
|
ASTM D638 |
|
弯曲模量
|
2480
|
MPa
|
ASTM D790 |
|
弯曲强度
|
101
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
130
|
J/m
|
ASTM D256 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度 (1.8 MPa, 未退火)
|
200
|
°C
|
ASTM D648 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
OSU峰值放热速率 2
|
< 55.0
|
kW/m²
|
FAR 25, AppF |
|
OSU总放热量 - 2分钟 2
|
< 20.0
|
kW·min/m²
|
FAR 25, AppF |
|
垂直燃烧-60秒 2
|
FAR 25, AppF | ||
|
滴液燃烧时间
|
无滴漏
|
|
|
|
燃烧时间
|
0.0
|
hr
|
|
|
长度
|
< 7.62
|
cm
|
|
|
毒气排放 2
|
BSS 7239/ATS 1000/ABD 0031 | ||
|
CO
|
< 10
|
ppm
|
|
|
HCL
|
< 1
|
ppm
|
|
|
HCN
|
< 1
|
ppm
|
|
|
HF
|
< 1
|
ppm
|
|
|
NO+NO2
|
< 1
|
ppm
|
|
|
SO2
|
< 1
|
ppm
|
|
|
烟雾密度 - Dmax，4 分钟 2
|
< 5.0
|
Ds
|
FAR 25, AppF |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
149 到 177
|
°C
|
|
|
干燥时间
|
4.0
|
hr
|
|
|
料筒后部温度
|
354 到 371
|
°C
|
|
|
料筒中部温度
|
360 到 377
|
°C
|
|
|
料筒前部温度
|
366 到 382
|
°C
|
|
|
射嘴温度
|
360 到 377
|
°C
|
|
|
加工（熔体）温度
|
366 到 388
|
°C
|
|
|
模具温度
|
107 到 163
|
°C
|
|
|
注射速度
|
快速
|
|
|
|
螺杆压缩比
|
2.0 : 1.0 到 3.0 : 1.0
|
|
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 2可燃性试验结果的目的不是为了反映这些或任何其他材料在实际火灾条件下的危险性。 |
亲，如果要PDF物性表，可以到物性下载栏目下载，或发邮件到：tjh@rjplastics.com索取！