GUR® 4120
超高分子量聚乙烯
Celanese Corporation
UHMWPE GUR 4120产品说明:
GUR 4120 UHMW-PE is a linear polyolefin resin in powder form with a molecular weight of approximately 5.0 MM g.mol calculated using Margolies' equation. The extremely high molecular weight of this resin yields several unique properties including superior abrasion resistance and highest impact strength of all standard grades. Outstanding properties include a low coefficient of friction that results in self-lubricating, non-stick surfaces after processing. The resin is normally processed by compression molding, ram extrusion or free sintering of porous parts.该产品在亚大地区供货商为深圳市仁捷塑胶原料有限公司，销售热线：18681139818，QQ：13931677。
泰科纳超高分子量聚乙烯UHMWPE GUR 4120物性
|
特性
|
|
|||
|
RoHS 合规性
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
|||
|
多点数据
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
0.928
|
g/cm³
|
ASTM D792 |
|
--
|
0.930
|
g/cm³
|
ISO 1183 |
|
熔流率（熔体流动速率） (190°C/21.6 kg)
|
< 0.10
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
< 0.010
|
%
|
|
|
平衡, 23°C, 50% RH
|
< 0.010
|
%
|
|
|
粘数
|
2400
|
cm³/g
|
ISO 307 |
|
Elongational Stress F - 150/10
|
0.220
|
MPa
|
ISO 1152-2 |
|
固有粘度
|
21
|
dl/g
|
ISO 1628-3 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度
|
|||
|
邵氏 D
|
63
|
|
ASTM D2240 |
|
邵氏 D, 15 秒
|
60
|
|
ISO 868 |
|
球压硬度 3
|
36.0
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
23°C
|
703
|
MPa
|
ASTM D638 |
|
--
|
720
|
MPa
|
ISO 527-2/1A/1 |
|
抗张强度
|
|||
|
屈服, 23°C
|
21.4
|
MPa
|
ASTM D638 |
|
屈服
|
17.0
|
MPa
|
ISO 527-2/1A/50 |
|
拉伸应变 (屈服)
|
20
|
%
|
ISO 527-2/1A/50 |
|
标称拉伸断裂应变
|
> 50
|
%
|
ISO 527-2/1A/50 |
|
拉伸蠕变模量
|
ISO 899-1 | ||
|
1 hr
|
460
|
MPa
|
|
|
1000 hr
|
230
|
MPa
|
|
|
摩擦系数 (与钢 - 动态)
|
0.10
|
|
内部方法 |
|
Wear by Sandslurry Method 4
|
100
|
|
内部方法 |
|
磨损量
|
100
|
|
内部方法 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
Charpy Impact Strength 5
|
210
|
kJ/m²
|
ISO 1152-2 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火
|
65.0
|
°C
|
ISO 75-2/B |
|
1.8 MPa, 未退火
|
42.0
|
°C
|
ISO 75-2/A |
|
维卡软化温度
|
80.0
|
°C
|
ASTM D1525, ISO 306/B50 |
|
线形热膨胀系数 - 流动
|
2.0E-4
|
cm/cm/°C
|
ASTM D696, ISO 11359-2 |
|
比热
|
内部方法 | ||
|
--
|
1840
|
J/kg/°C
|
|
|
23°C
|
1840
|
J/kg/°C
|
|
|
导热系数 (23°C)
|
0.41
|
W/m/K
|
内部方法 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
|||
|
--
|
> 1.0E+13
|
ohm
|
ASTM D257 |
|
--
|
> 1.0E+12
|
ohm
|
IEC 60093 |
|
体积电阻率
|
|||
|
--
|
> 1.0E+15
|
ohm·cm
|
ASTM D257 |
|
--
|
> 1.0E+14
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
45
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
1 MHz
|
3.00
|
|
ASTM D150, IEC 60250 |
|
100 Hz
|
2.10
|
|
IEC 60250 |
|
耗散因数
|
IEC 60250 | ||
|
100 Hz
|
3.9E-4
|
|
|
|
1 MHz
|
1.0E-3
|
|
|
|
漏电起痕指数
|
600
|
V
|
IEC 60112 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.60 mm)
|
HB
|
|
UL 94 |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 2UL 黄卡含有 UL 验证的易燃性和电气特性。UL Prospector 持续努力在 Prospector 中将黄卡链接至单个塑料材料，然而此列表可能未包括所有相应链接。重要的是，我们对 Prospector 中找到的这些黄卡和塑料材料之间的关联进行验证。如需完整的黄卡列表，请访问 UL 黄卡搜索。 |
| 330 sec |
| 4Based on GUR 4120=100 |
| 514° V-notch both sides |