GUR® 4152
超高分子量聚乙烯
Celanese Corporation
UHMWPE GUR 4152产品说明:
GUR 4152 UHMW-PE is a linear polyolefin resin in powder form with a molecular weight of approximately 7.7 MM g/mol calculated using Margolies' equation. The extremely high molecular weight of this resin yields several unique properties including superior abrasion resistance and impact strength. This and GUR 4150 resins have the best abrasion resistance of all standard grades. Outstanding properties include a low coefficient of friction that results in self-lubricating, non-stick surfaces after processing. The resin is normally processed by compression molding or ram extrusion.该产品在亚大地区供货商为深圳市仁捷塑胶原料有限公司，销售热线：18681139818，QQ：13931677。
泰科纳超高分子量聚乙烯UHMWPE GUR 4152物性数据：
|
特性
|
|
|||
|
RoHS 合规性
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度
|
0.930
|
g/cm³
|
ISO 1183 |
|
熔流率（熔体流动速率） (190°C/21.6 kg)
|
< 0.10
|
g/10 min
|
ASTM D1238, ISO 1133 |
|
吸水率 (平衡, 23°C, 50% RH)
|
< 0.010
|
%
|
ISO 62 |
|
粘数
|
3400
|
cm³/g
|
ISO 307 |
|
Elongational Stress F - 150/10
|
0.410
|
MPa
|
ISO 1152-2 |
|
固有粘度
|
28
|
dl/g
|
ISO 1628-3 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度
|
|||
|
邵氏 D
|
61
|
|
ASTM D2240 |
|
邵氏 D, 15 秒
|
61
|
|
ISO 868 |
|
球压硬度 2
|
35.0
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
23°C
|
689
|
MPa
|
ASTM D638 |
|
--
|
680
|
MPa
|
ISO 527-2/1A/1 |
|
抗张强度
|
|||
|
屈服, 23°C
|
21.4
|
MPa
|
ASTM D638 |
|
屈服
|
17.0
|
MPa
|
ISO 527-2/1A/50 |
|
断裂, 23°C
|
35.0
|
MPa
|
ASTM D638 |
|
断裂
|
35.0
|
MPa
|
ISO 527-2/1A/50 |
|
伸长率
|
|||
|
屈服, 23°C
|
< 20
|
%
|
ASTM D638 |
|
屈服
|
20
|
%
|
ISO 527-2/1A/50 |
|
断裂, 23°C
|
> 300
|
%
|
ASTM D638 |
|
标称拉伸断裂应变
|
300
|
%
|
ISO 527-2/1A/50 |
|
拉伸蠕变模量
|
ISO 899-1 | ||
|
1 hr
|
430
|
MPa
|
|
|
1000 hr
|
220
|
MPa
|
|
|
摩擦系数 (与钢 - 动态)
|
0.10
|
|
内部方法 |
|
Wear by Sandslurry Method 3
|
80.0
|
|
内部方法 |
|
磨损量
|
80.0
|
|
内部方法 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
Charpy Impact Strength 4
|
130
|
kJ/m²
|
ISO 1152-2 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火
|
65.0
|
°C
|
ISO 75-2/B |
|
1.8 MPa, 未退火
|
42.0
|
°C
|
ISO 75-2/A |
|
维卡软化温度
|
80.0
|
°C
|
ASTM D1525, ISO 306/B50 |
|
线形热膨胀系数 - 流动
|
2.0E-4
|
cm/cm/°C
|
ISO 11359-2 |
|
比热
|
内部方法 | ||
|
--
|
1840
|
J/kg/°C
|
|
|
23°C
|
1840
|
J/kg/°C
|
|
|
导热系数 (23°C)
|
0.41
|
W/m/K
|
内部方法 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
> 1.0E+12
|
ohm
|
IEC 60093 |
|
体积电阻率
|
> 1.0E+14
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
45
|
kV/mm
|
IEC 60243-1 |
|
相对电容率
|
IEC 60250 | ||
|
100 Hz
|
2.10
|
|
|
|
1 MHz
|
3.00
|
|
|
|
耗散因数
|
IEC 60250 | ||
|
100 Hz
|
4.0E-4
|
|
|
|
1 MHz
|
1.0E-3
|
|
|
|
漏电起痕指数
|
600
|
V
|
IEC 60112 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.60 mm)
|
HB
|
|
UL 94 |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 230 sec |
| 3Based on GUR 4120=100 |
| 414° V-notch both sides |