Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness,

strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic pla

stics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resis

tance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer co

ntent increases impact strength. Tenite™ cellulose plastics are available in natural, clear, selected a

mbers, or smoke transparents and black translucents. Color concentrates are available in let-down

ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-18 has a plasticizer level of 18% an

d contains an odor mask.

基本信息
添加剂	增塑剂 (18%)
特性	高光 经增塑 可更新资源 良好的强度 清晰度，高 韧性良好 柔软 硬度高
用途	安全设备 镜架 眼镜
外观	黑色 琥珀色 清晰/透明 自然色
形式	粒子

物理性能	额定值	单位制	测试方法
比重	1.17	g/cm³	ASTM D792
吸水率 (23°C, 24 hr)	1.3	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级, 23°C)	26		ASTM D785

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 23°C	23.5	MPa	ASTM D638
断裂, 23°C	30.7	MPa	ASTM D638
伸长率 (断裂, 23°C)	50	%	ASTM D638
弯曲模量 (23°C)	1030	MPa	ASTM D790
弯曲强度 (屈服, 23°C)	30.4	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度			ASTM D256
-40°C	110	J/m	ASTM D256
23°C	360	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度 1			ASTM D648
0.45 MPa, 退火	75.0	°C	ASTM D648
1.8 MPa, 退火	61.0	°C	ASTM D648
维卡软化温度 2	94.0	°C	ASTM D1525

补充信息	额定值	单位制	测试方法
Soluble Matter Loss (23°C)	0.10	%	ASTM D570
Weight Loss on Heating - 72 hrs (80°C)	0.90	%	ASTM D707