Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness

, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic pl

astics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resi

stance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer c

ontent increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected

ambers or smoke transparents and black translucents. Color concentrates are available in let-down

ratios from 10:1 to 40:1. ™Tenite™ Cellulose Acetate Butyrate 572-12 contains an odor mask lubrica

nt and an ultra-violet inhibitor(UVI). It has a plasticizer level of 12%.

基本信息
添加剂	润滑剂 增塑剂 (12%) 紫外线稳定剂
特性	高光 经增塑 抗紫外线性能良好 可更新资源 良好的强度 气味低到无 清晰度，高 韧性良好 柔软 润滑 硬度高
用途	薄膜 片材 型材
外观	黑色 琥珀色 清晰/透明 自然色
形式	粒子

物理性能	额定值	单位制	测试方法
比重	1.19	g/cm³	ASTM D792
吸水率 (23°C, 24 hr)	1.3	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级, 23°C)	87		ASTM D785

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 23°C	33.8	MPa	ASTM D638
断裂, 23°C	34.0	MPa	ASTM D638
伸长率 (断裂, 23°C)	23	%	ASTM D638
弯曲模量 (23°C)	1300	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度			ASTM D256
-40°C	98	J/m	ASTM D256
23°C	350	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度 1			ASTM D648
0.45 MPa, 退火	83.0	°C	ASTM D648
1.8 MPa, 退火	78.0	°C	ASTM D648

补充信息	额定值	单位制	测试方法
Weight Loss on Heating 2(80°C)	0.40	%	ASTM D707