聚偏二氟乙烯 Kynar Flex® 2800-00产品说明:
KYNAR FLEX® 2800-00 is a pelletized, semi-crystalline VF 2 based copolymer. KYNAR FLEX® 2800-00 has been specifically designed for use in wire and cable constructions and other uses requiring high flexibility and improved resistance to impact. For chemical applications, it can be extruded into sheets and tubing. KYNAR FLEX® 2800-00 can be injection molded.
ADVANTAGES:
Improved flexibility at subzero temperatures to -20°C(-4°F)
Improved stress crack resistance to -20°C(-4°F)
Improved elongation at break
ADDITIONAL CHARACTERISTICS:
Easy processability using conventional equipment
Excellent thermal stability
Excellent chemical resistance
Retains properties after aging
Meets UL 910 smoke and flame requirements as cable jacket
UL temperature rating 125°C
Radiation crosslinking
法国阿科玛(聚偏二氟乙烯)PVDF 2800-00物性数据
法国阿科玛(聚偏二氟乙烯)PVDF树脂在中国大陆主要供应商为仁捷塑胶公司，财富热线：18681139818，QQ:13931677，联系人：唐生。
|
特性
|
|
|||
|
用途
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
|||
|
多点数据
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.77 到 1.80
|
g/cm³
|
ASTM D792 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 (邵氏 D, 23°C)
|
60 到 70
|
|
ASTM D2240 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度
|
ASTM D638 | ||
|
屈服, 23°C
|
20.0 到 34.5
|
MPa
|
|
|
断裂, 23°C
|
17.2 到 34.5
|
MPa
|
|
|
伸长率 (断裂, 23°C)
|
100 到 300
|
%
|
ASTM D638 |
|
弯曲模量 (23°C)
|
483 到 758
|
MPa
|
ASTM D790 |
|
弯曲强度 (23°C)
|
20.7 到 34.5
|
MPa
|
ASTM D790 |
|
压缩强度 (23°C)
|
31.0 到 41.4
|
MPa
|
ASTM D695 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
熔融峰值温度
|
140 到 145
|
°C
|
ASTM D3418 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率 3 (20°C)
|
2.0E+14
|
ohm·cm
|
ASTM D257 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (232°C, 100 sec^-1)
|
2200 到 2700
|
Pa·s
|
ASTM D3835 |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
亲，如果要PDF物性表，可以到物性下载栏目下载，或发邮件到：tjh@rjplastics.com索取！
温馨提示：仁捷公司免费24小时提供塑胶原料注塑成型技术支持,咨询热线：18681139818，联系人：唐生
Tag: 法国阿科玛 ,聚偏二氟乙烯 ,PVDF