聚偏二氟乙烯 Kynar Flex® 2850-00产品说明:
KYNAR FLEX® 2850-00 is a pelletized, semi-crystalline VF2 based copolymer. The powder form of this resin is designated KYNAR FLEX® 2851-00. KYNAR FLEX® 2850-00 has been specifically designed for use in wire and cable constructions which require an Underwriters Laboratories temperature of 150°C. It is close in physical performance to KYNAR® PVDF homopolymer grades, but has a higher flexibility. KYNAR FLEX® 2850-00 is also used in chemical applications as extruded sheet and pipe liners.
ADDITIONAL CHARACTERISTICS:
Excellent thermal stability
Excellent abrasion resistance
Excellent purity and chemical resistance
Impervious to UV degradation
Self extinguishing material
Extremely low smoke emission characteristics
Pigmentable
法国阿科玛(聚偏二氟乙烯)PVDF 2850-00物性数据
法国阿科玛(聚偏二氟乙烯)PVDF树脂在中国大陆主要供应商为仁捷塑胶公司，财富热线：18681139818，QQ:13931677，联系人：唐生。
|
特性
|
|
|||
|
用途
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
|||
|
多点数据
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.77 到 1.80
|
g/cm³
|
ASTM D792 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 (邵氏 D, 23°C)
|
70 到 75
|
|
ASTM D2240 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度
|
ASTM D638 | ||
|
屈服, 23°C
|
31.0 到 41.4
|
MPa
|
|
|
断裂, 23°C
|
27.6 到 48.3
|
MPa
|
|
|
伸长率 (断裂, 23°C)
|
30 到 200
|
%
|
ASTM D638 |
|
弯曲模量 (23°C)
|
1030 到 1240
|
MPa
|
ASTM D790 |
|
弯曲强度 (23°C)
|
20.7 到 34.5
|
MPa
|
ASTM D790 |
|
压缩强度 (23°C)
|
41.4 到 58.6
|
MPa
|
ASTM D695 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
熔融峰值温度
|
155 到 160
|
°C
|
ASTM D3418 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率 3 (20°C)
|
2.0E+14
|
ohm·cm
|
ASTM D257 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (232°C, 100 sec^-1)
|
2300 到 2700
|
Pa·s
|
ASTM D3835 |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
亲，如果要PDF物性表，可以到物性下载栏目下载，或发邮件到：tjh@rjplastics.com索取！
温馨提示：仁捷公司免费24小时提供塑胶原料注塑成型技术支持,咨询热线：18681139818，联系人：唐生
Tag: 法国阿科玛 ,聚偏二氟乙烯 ,PVDF