聚偏二氟乙烯 Kynar Flex® 2850-02产品说明:
KYNAR FLEX® 2850-02 is a pelletized, semi-crystalline VF2 based copolymer.
KYNAR FLEX® 2850-02 has been specifically designed for use in wire and cable constructions which require an Underwriters Laboratories temperature of 150°C and a Limiting Oxygen Index (LOI) of at least 75.
KYNAR FLEX® 2850-02 is easily processed and has excellent physical, mechanical, thermal and flame resistant characteristics. KYNAR FLEX® 2850-02 meets the smoke and flame requirements of UL 910 and ASTM E84 (the Modified Steiner Tunnel Test). This copolymer is commonly used for pipe, wire jacketing, conduits, and in injection molded parts.
ADDITIONAL CHARACTERISTICS:
Excellent thermal stability
Excellent abrasion resistance
Impervious to UV degradation
Self extinguishing material
Extremely low smoke emission characteristics
0/0 rating in ASTM E-84/UL 723
法国阿科玛(聚偏二氟乙烯)PVDF 2850-02物性数据
法国阿科玛(聚偏二氟乙烯)PVDF树脂在中国大陆主要供应商为仁捷塑胶公司，财富热线：18681139818，QQ:13931677，联系人：唐生。
|
特性
|
|
|||
|
用途
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.77 到 1.80
|
g/cm³
|
ASTM D792 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 (邵氏 D, 23°C)
|
70 到 75
|
|
ASTM D2240 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度
|
ASTM D638 | ||
|
屈服, 23°C
|
31.0 到 41.4
|
MPa
|
|
|
断裂, 23°C
|
27.6 到 48.3
|
MPa
|
|
|
伸长率 (断裂, 23°C)
|
30 到 200
|
%
|
ASTM D638 |
|
弯曲模量 (23°C)
|
1030 到 1240
|
MPa
|
ASTM D790 |
|
弯曲强度 (23°C)
|
20.7 到 34.5
|
MPa
|
ASTM D790 |
|
压缩强度 (23°C)
|
41.4 到 58.6
|
MPa
|
ASTM D695 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
熔融峰值温度
|
155 到 160
|
°C
|
ASTM D3418 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率 3 (20°C)
|
2.0E+14
|
ohm·cm
|
ASTM D257 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (232°C, 100 sec^-1)
|
1600 到 2000
|
Pa·s
|
ASTM D3835 |