聚偏二氟乙烯 Kynar Flex® 3120-50产品说明:
KYNAR FLEX® 3120-50 is a pelletized semi-crystalline VF2 based copolymer. It can be molded or extruded and has a useful temperature range from -40°C - 150°C. KYNAR FLEX® 3120-50 has a UL RTI of 150°C
KYNAR FLEX® 3121-50 can be used in compounding for wire and cable as well as other extrusion applications.
KYNAR FLEX® 3121-50 is a specially designed powder used as a polymer process aid (PPA) for polyolefins. The use of KYNAR FLEX® 3120-50 or KYNAR FLEX 3121-50 at 200 - 1000 ppm levels reduces extruder pressure, improves surface finish, reduces die build up, and improves gauge control.
法国阿科玛(聚偏二氟乙烯)PVDF 3121-50物性数据
法国阿科玛(聚偏二氟乙烯)PVDF树脂在中国大陆主要供应商为仁捷塑胶公司，财富热线：18681139818，QQ:13931677，联系人：唐生。
|
特性
|
|
|||
|
用途
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.76 到 1.79
|
g/cm³
|
ASTM D792 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 (邵氏 D, 23°C)
|
65 到 70
|
|
ASTM D2240 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度
|
ASTM D638 | ||
|
屈服, 23°C
|
24.1 到 34.5
|
MPa
|
|
|
断裂, 23°C
|
34.5 到 48.3
|
MPa
|
|
|
伸长率 (断裂, 23°C)
|
300 到 550
|
%
|
ASTM D638 |
|
弯曲模量 (23°C)
|
621 到 827
|
MPa
|
ASTM D790 |
|
弯曲强度 (23°C)
|
20.7 到 34.5
|
MPa
|
ASTM D790 |
|
压缩强度 (23°C)
|
31.0 到 41.4
|
MPa
|
ASTM D695 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
熔融峰值温度
|
161 到 168
|
°C
|
ASTM D3418 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率 2 (20°C)
|
2.0E+14
|
ohm·cm
|
ASTM D257 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (232°C, 100 sec^-1)
|
2000 到 2600
|
Pa·s
|
ASTM D3835 |