Arkema Kynar® 370聚偏二氟乙烯产品说明:
碳纤维增强材料
KYNAR® 370 resin is a pelletized, semi-crystalline polymer of vinylidene fluoride. It is a versatile engineering plastic with an outstanding balance of physical and chemical properties that qualify it for high performance service in a wide variety of applications. It is a fluoropolymer capable of being fabricated on standard processing equipment.
KYNAR® 370 is a low viscosity grade that has been filled with carbon to enhance physical properties. Mold shrinkage and thermal expansion are decreased by the addition of carbon. The shrinkage in molding of this product is very similar to that of polypropylene. This modification also increases the tensile strength, modulus, and heat deflection temperature substantially. KYNAR® 370 can be injection molded and extruded.
法国阿科玛(聚偏二氟乙烯)PVDF 370物性数据
法国阿科玛(聚偏二氟乙烯)PVDF树脂在中国大陆主要供应商为仁捷塑胶公司，财富热线：18681139818，QQ:13931677，联系人：唐生。
|
填料/增强材料
|
|
|||
|
特性
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.84 到 1.88
|
g/cm³
|
ASTM D792 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度 (邵氏 D, 23°C)
|
74 到 79
|
|
ASTM D2240 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度
|
ASTM D638 | ||
|
屈服, 23°C
|
34.5 到 55.2
|
MPa
|
|
|
断裂, 23°C
|
37.9 到 55.2
|
MPa
|
|
|
伸长率 (断裂, 23°C)
|
0.0 到 20
|
%
|
ASTM D638 |
|
弯曲模量 (23°C)
|
5520 到 6890
|
MPa
|
ASTM D790 |
|
弯曲强度 (23°C)
|
138 到 207
|
MPa
|
ASTM D790 |
|
压缩强度 (23°C)
|
138 到 172
|
MPa
|
ASTM D695 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
熔融峰值温度
|
165 到 172
|
°C
|
ASTM D3418 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率 2 (20°C)
|
1.0E+11
|
ohm·cm
|
ASTM D257 |
| 充模分析 |
额定值
|
单位制
|
测试方法
|
|
熔体粘度 (232°C, 100 sec^-1)
|
800 到 1300
|
Pa·s
|
ASTM D3835 |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
亲，如果要PDF物性表，可以到物性下载栏目下载，或发邮件到：tjh@rjplastics.com索取！
温馨提示：仁捷公司免费24小时提供塑胶原料注塑成型技术支持,咨询热线：18681139818，联系人：唐生
Tag: 法国阿科玛 ,聚偏二氟乙烯 ,PVDF