Sarlink ML-1100 is a general purpose thermoplastic elastomer series, available in NAT and BLK designed for automotive interior applications. Sarlink ML-1180N NAT is a medium hardness, high density, filled grade suitable for injection molding.

基本信息
特性	Sunlight Resistant 高比重 高密度 良好的成型性能 良好的柔韧性 良好的撕裂强度 良好的着色性 良好粘结性 流动性高 耐化学性良好 韧性良好 填充 有弹性 中等硬度
用途	垫圈 汽车领域的应用 汽车内部零件 柔软触感应用 柔软的把手 通用 橡胶取代 旋钮
RoHS 合规性	RoHS 合规
外观	自然色
形式	粒子
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度	1.18	g/cm³	ISO 1183
熔流率（熔体流动速率） (190°C/2.16 kg)	14	g/10 min	ASTM D1238

硬度	额定值	单位制	测试方法
肖氏硬度			ISO 868
邵氏 A, 1 秒, 注塑	81		ISO 868
邵氏 A, 5 秒, 注塑	79		ISO 868
邵氏 A, 15 秒, 注塑	78		ISO 868

弹性体	额定值	单位制	测试方法
拉伸应力 1			ISO 37
横向流量 : 100%应变	2.55	MPa	ISO 37
流量 : 100%应变	3.40	MPa	ISO 37
拉伸应力 2			ISO 37
横向流量 : 断裂	6.40	MPa	ISO 37
流量 : 断裂	6.30	MPa	ISO 37
伸长率 3			ISO 37
横向流量 : 断裂	730	%	ISO 37
流量 : 断裂	630	%	ISO 37
撕裂强度 4			ISO 34-1
横向流量	31	kN/m	ISO 34-1
流量	26	kN/m	ISO 34-1
压缩永久变形 5			ISO 815
23°C, 22 hr	37	%	ISO 815
70°C, 22 hr	53	%	ISO 815
90°C, 70 hr	70	%	ISO 815
125°C, 70 hr	95	%	ISO 815

老化	额定值	单位制	测试方法
空气中拉伸强度的变化率 6			ISO 188
横向流量 : 110°C, 1008 hr	-2.3	%	ISO 188
流量 : 110°C, 1008 hr	-8.6	%	ISO 188
横向流量 : 100% 应变 110°C, 1008 hr	10	%	ISO 188
流量 : 100% 应变 110°C, 1008 hr	17	%	ISO 188
横向流量 : 125°C, 168 hr	-2.5	%	ISO 188
流量 : 125°C, 168 hr	-12	%	ISO 188
横向流量 : 100% 应变 125°C, 168 hr	8.4	%	ISO 188
流量 : 100% 应变 125°C, 168 hr	16	%	ISO 188
在空气中断裂时拉伸应力变化 7			ISO 188
横向流量 : 110°C, 1008 hr	-1.0	%	ISO 188
流量 : 110°C, 1008 hr	-11	%	ISO 188
横向流量 : 125°C, 168 hr	1.0	%	ISO 188
流量 : 125°C, 168 hr	-13	%	ISO 188
空气中邵氏硬度的变化率			ISO 188
邵氏 A, 110°C, 1008 hr 8	2.8		ISO 188
邵氏 A, 110°C, 1008 hr 9	2.2		ISO 188
邵氏 A, 110°C, 1008 hr 10	1.1		ISO 188
邵氏 A, 125°C, 168 hr 11	3.5		ISO 188
邵氏 A, 125°C, 168 hr 12	2.7		ISO 188
邵氏 A, 125°C, 168 hr 13	1.3		ISO 188

充模分析	额定值	单位制	测试方法
表观粘度 (200°C, 206 sec^-1)	136	Pa·s	ASTM D3835

法律声明

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

注射	额定值	单位制
料筒后部温度	171 到 193	°C
料筒中部温度	177 到 199	°C
料筒前部温度	182 到 204	°C
射嘴温度	188 到 210	°C
加工（熔体）温度	188 到 210	°C
模具温度	16 到 32	°C
注塑压力	1.38 到 6.89	MPa
注射速度	中等偏快
背压	0.172 到 0.345	MPa
螺杆转速	50 到 100	rpm
垫层	3.81 到 25.4	mm

注射说明
Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C).

备注
1 .	类型 1, 510 mm/min
2 .	类型 1, 510 mm/min
3 .	类型 1, 510 mm/min
4 .	B 方法，直角形试样（不割口）, 510 mm/min
5 .	类型 A
6 .	类型 1
7 .	类型 1
8 .	15 sec
9 .	5 sec
10 .	1 sec
11 .	15 sec
12 .	5 sec
13 .	1 sec