3M™ Dyneon™ Ultra High Purity PFA FLEX8502UHPZ family exhibits improved environmental stress crack resistance (ESCR) to stress cracking chemicals or such agents that specifically contain fluorosurfactants. In addition, this family offers very low levels of extractable ions, makingit suitable for critical wet chemical processes in the semiconductor industry.

Features

• Significantly longer life in fluorosurfactant containing fluids

• Extremely low level of extractable ions

• Smoother surfaces

• Improved clarity

• Improved flexibility

• Service temperature range up to 240 °C

• Extreme stress crack resistance
• M™ Dyneon™ Fluoroplastic PFA FLEX8502UHPZ 物性表

  基本信息
  特性	Low (to None) Ion Content 纯度高 低萃取物 高 ESCR（抗应力开裂）
  形式	粒子
  加工方法	吹塑成型 树脂传递成型 压缩模塑

  物理性能	额定值	单位制	测试方法
  密度	2.15	g/cm³	ISO 12086
  熔流率（熔体流动速率） (372°C/5.0 kg)	2.0	g/10 min	ISO 1133

  硬度	额定值	单位制	测试方法
  肖氏硬度 (邵氏 D)	60		ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸应力 (断裂, 23°C)	35.0	MPa	ISO 527-1
  拉伸应变 (断裂, 23°C)	330	%	ISO 527-1
  弯曲模量	600	MPa	ASTM D790

  热性能	额定值	单位制	测试方法
  熔融温度	300	°C	ISO 12086

  可燃性	额定值	单位制	测试方法
  极限氧指数	> 95	%	ASTM D2863