3M™ Dyneon™ Fluoroplastic PFA 6515TZ (a fully fluorinated copolymer of tetrafluoroethylene and perfluorovinylether) has exceptional heat resistance, excellent electrical properties and excellent chemical and weather resistance.

Features

• Wide service temperature range

• Excellent, almost universal resistance to solvents and chemicals

• Extremely high weathering resistance and UV stability

• Excellent electrical insulation properties, e.g.: dielectric breakdown strength, dielectric constant

• High limiting oxygen index: Does not support combustion

• Smooth surfaces

• Good non-stick characteristics

• Good low-friction properties

• Broad processing window

• Improved mold release property

• Improved stress crack resistance

• High transparency
• M™ Dyneon™ Fluoroplastic PFA 6515TZ 物性表

  基本信息
  特性	低摩擦系数 共聚物 抗溶剂性 抗紫外线性能良好 良好的电气性能 耐化学性良好 耐气候影响性能良好 耐热性，高 脱模性能良好 无粘性 中等透明度
  用途	电线电缆应用
  形式	粒子
  加工方法	电线&线缆挤出成型 注射成型

  物理性能	额定值	单位制	测试方法
  密度	2.15	g/cm³	ISO 12086
  熔流率（熔体流动速率） (372°C/5.0 kg)	15	g/10 min	ISO 1133

  硬度	额定值	单位制	测试方法
  肖氏硬度 (邵氏 D)	60		ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸应力 (断裂, 23°C)	28.0	MPa	ISO 527-1
  拉伸应变 (断裂, 23°C)	420	%	ISO 527-1
  弯曲模量	620	MPa	ASTM D790

  热性能	额定值	单位制	测试方法
  熔融温度	308	°C	ISO 12086

  可燃性	额定值	单位制	测试方法
  极限氧指数	> 95	%	ASTM D2863

  注射	额定值	单位制
  加工（熔体）温度	250 到 400	°C

  挤出	额定值	单位制
  熔体温度	< 400	°C

H