3M™ Dyneon™ Ultra High Purity PFA 6515UHPZ grades are a new series of ultra-high purity fluoro-thermoplastics. These resins were developed for high-purity applications requiring ultra-low levels of metal and other cation and anion extractions, such as in the semiconductor market. The Dyneon PFA UHP Z family comprises grades that can be compression-molded, transfer-molded, extruded, injection-molded or blow-molded.

Features

• Extremely low level of extractable trace elements

• Extremely low levels of fluoride ions and other anions

• Service temperature range up to 260 °C

• Excellent chemical resistance

• UHP packaged to assure clean, contamination-free product
• M™ Dyneon™ Fluoroplastic PFA 6515UHPZ 物性表

  基本信息
  特性	Low (to None) Ion Content 纯度高 低萃取物 耐化学性良好
  用途	半导体模制化合物
  形式	粒子
  加工方法	吹塑成型 挤出 树脂传递成型 压缩模塑 注射成型

  物理性能	额定值	单位制	测试方法
  密度	2.15	g/cm³	ISO 12086
  熔流率（熔体流动速率） (372°C/5.0 kg)	15	g/10 min	ISO 1133

  硬度	额定值	单位制	测试方法
  肖氏硬度 (邵氏 D)	60		ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸应力 (断裂, 23°C)	26.0	MPa	ISO 527-1
  拉伸应变 (断裂, 23°C)	450	%	ISO 527-1
  弯曲模量	620	MPa	ASTM D790

  热性能	额定值	单位制	测试方法
  熔融温度	309	°C	ISO 12086

  可燃性	额定值	单位制	测试方法
  极限氧指数	> 95	%	ASTM D2863

  注射	额定值	单位制
  加工（熔体）温度	250 到 400	°C

  挤出	额定值	单位制
  熔体温度	< 400	°C