PRIMACOR™ 3150 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating resin for flexible packaging applications. It provides excellent adhesion to metallic, paper and polyethylene substrates, and offers good draw- down, heat sealability and oil and grease resistance.

• For extrusion/coextrusion coating and laminating applications

• Adhesion to metallic, paper and polyethylene substrates

• Cost effective sealant or tie resin for foil-based structures

• Moisture insensitivity

Complies with:

• U.S. FDA 21 CFR 177.1310(a)(1)

• EU, No 10/2011

Consult the regulations for complete details.

基本信息
机构评级	FDA 21 CFR 177.1310 (a) 1 欧洲 No 10/2011
形式	粒子
加工方法	挤出涂层

物理性能	额定值	单位制	测试方法
比重	0.924	g/cm³	ASTM D792, ISO 1183
熔流率（熔体流动速率） 1(190°C/2.16 kg)	11	g/10 min	ASTM D1238, ISO 1133
共聚单体含量 2	3.0	%	内部方法

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638, ISO 527-2
屈服, 模压成型	8.79	MPa	ASTM D638, ISO 527-2
断裂, 模压成型	12.3	MPa	ASTM D638, ISO 527-2
伸长率 (断裂, 模压成型)	590	%	ASTM D638, ISO 527-2

热性能	额定值	单位制	测试方法
维卡软化温度	88.9	°C	ASTM D1525, ISO 306
溶融温度（DSC）	104	°C	内部方法

挤出	额定值	单位制	测试方法
熔体温度	260 到 290	°C
内缩量 (288°C, 25.4 µm)	63.5	mm	内部方法
最小涂层厚度	10	µm	内部方法
最小涂层重量	9.8	g/m²	内部方法

挤压说明
挤出涂层薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。 螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D 模具间隙：20 密尔 (0.508 mm) 模具：30 英寸模具切边至 24 英寸 熔体温度：550°F (288°C) 输出：250 磅/小时 气隙：6 英寸 (152 mm)