LOTADER® HX8290 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

Applications
Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, LOTADER ® HX8290 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds such as halogen free flame retardant wires and cables.

基本信息
添加剂	卤素
特性	三元共聚物
用途	电线电缆应用 塑料改性 粘合剂
加工方法	挤出

物理性能	额定值	单位制	测试方法
密度	0.940	g/cm³	ISO 1183, ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	70	g/10 min	ASTM D1238, ISO 1133
Ethyl Acrylate Content	17.0	wt%
Maleic Anhydride Content	2.8	wt%

机械性能	额定值	单位制	测试方法
抗张强度 (断裂, 模压成型)	6.00	MPa	ASTM D638, ISO 527-2
伸长率 (断裂, 模压成型)	700	%	ASTM D638, ISO 527-2
弯曲模量 (模压成型)	30.0	MPa	ASTM D790, ISO 178

热性能	额定值	单位制	测试方法
维卡软化温度	< 40.0	°C	ISO 306/A, ASTM D1525 1
熔融温度	85.0	°C	ISO 11357-3

备注
1 .	压 力1 (10N)