• Low heat seal temperature, high hot tack

• High gloss, excellent clarity

• Excellent water, grease and oil resistance

Complies with

• U.S. FDA 21 CFR 177.1310(a)(2)

PRIMACOR™ 5990I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other substrates. In dispersion form, it is a versatile binder for nonwoven fibers, including polypropylene, polyester, glass, nylon and others.

Applications:

• Adhesives

• Laminations

• Foil priming

• Heat sealing

• Nonwoven binding

• Metal/paper coating

Outstanding Properties:

• Dispersible in aqueous amines and alkali

• "Clean" dispersion requires no salts, surfactants or solvents

• Dispersions use existing waterbourne application equipment

• High hot tack

• Low odor
• PRIMACOR™ 5990I 物性表

  基本信息
  机构评级	FDA 21 CFR 177.1310 (a) 2
  形式	粒子
  加工方法	涂层

  物理性能	额定值	单位制	测试方法
  比重	0.955	g/cm³	ASTM D792, ISO 1183
  熔流率（熔体流动速率）			ASTM D1238, ISO 1133
  125°C/2.16 kg 1	65	g/10 min	ASTM D1238, ISO 1133
  190°C/2.16 kg 2	1300	g/10 min	ASTM D1238, ISO 1133
  共聚单体含量 3	20.0	%	内部方法

  机械性能	额定值	单位制	测试方法
  拉伸模量 - 2% 正割 (模压成型)	22.1	MPa	ASTM D638, ISO 527-2
  抗张强度 (断裂, 模压成型)	6.21	MPa	ASTM D638, ISO 527-2
  伸长率 (断裂, 模压成型)	350	%	ASTM D638, ISO 527-2

  热性能	额定值	单位制	测试方法
  维卡软化温度	40.0	°C	ASTM D1525, ISO 306
  溶融温度（DSC）	75.0	°C	内部方法

  挤压说明
  用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。

  备注
  1 .	如同在生产时测量的一样。
  2 .	熔体指数值和熔体流动速率相关联（ASTM D 1238 条件为 125°C/2.16kg）。
  3 .	通过 Dow 属性方法测量的共聚单体含量，和 ASTM D 4094 相比具有相同的精确性。