• Low heat seal temperature, high hot tack

• High gloss, excellent clarity

• Excellent grease and oil resistance, water hold-out and excellent product resistance for flexible packaging applications

• Complies with:

• U.S. FDA 21 CFR 177.1310(a)(2)

Consult the regulations for complete details.

PRIMACOR™ 5980I is an ethylene acrylic acid copolymer with excellent adhesion to metallic, cellulosic, glass and other polar substrates. In dispersion form, it can be used effectively as a foil primer or laminating adhesive for polyethylene and metallized substrates.

Applications:

• Adhesives

• Laminations

• Foil priming

• Heat sealing

• Nonwoven binding

• Metal/paper coating

Outstanding Properties:

• Dispersible in aqueous amines and alkali

• "Clean" dispersion requires no salts, surfactants or solvents

• Dispersions use existing waterbourne application equipment

• High hot tack

• Low odor
• RIMACOR™ 5980I 物性表

  基本信息
  机构评级	FDA 21 CFR 177.1310 (a) 2
  形式	粒子
  加工方法	涂层

  物理性能	额定值	单位制	测试方法
  比重	0.958	g/cm³	ASTM D792, ISO 1183
  熔流率（熔体流动速率）			ASTM D1238, ISO 1133
  125°C/2.16 kg 1	14	g/10 min	ASTM D1238, ISO 1133
  190°C/2.16 kg 2	300	g/10 min	ASTM D1238, ISO 1133
  共聚单体含量 3	20.5	%	内部方法

  硬度	额定值	单位制	测试方法
  肖氏硬度 (邵氏 D)	50		ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸模量 - 2% 正割 (模压成型)	33.1	MPa	ASTM D638, ISO 527-2
  抗张强度 (断裂, 模压成型)	9.65	MPa	ASTM D638, ISO 527-2
  伸长率 (断裂, 模压成型)	390	%	ASTM D638, ISO 527-2

  热性能	额定值	单位制	测试方法
  维卡软化温度	42.2	°C	ASTM D1525, ISO 306
  溶融温度（DSC）	77.2	°C	内部方法

  挤压说明
  用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。

  备注
  1 .	如同在生产时测量的一样。
  2 .	熔体指数值和熔体流动速率相关联（ASTM D 1238 条件为 125°C/2.16kg）。
  3 .	通过 Dow 属性方法测量的共聚单体含量，和 ASTM D 4094 相比具有相同的精确性。