PREPERM® L700HF is a special compound with elevated dielectric constants of 7.0.
PREPERM® L700HF is a special compound based on Premix proprietary PPE technology. E

xtremely low dissipation factor (< 0.001) makes PREPERM® L700HF an excellent material f

or high frequency applications. PREPERM® L700HF offers stable dielectric constant over w

ide frequency and wide temperature range. PREPERM® L700HF is modified for injection m

oulding.

Applications include structural parts for antennas in base stations, point to point, wlan, mob

ile phones etc. Devices made out of PREPERM® can operate at very high frequencies as PRE

PERM® offers stable performance even at 120 GHz.

基本信息
用途	电气/电子应用领域 电气元件
RoHS 合规性	RoHS 合规
形式	颗粒
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度	1.98	g/cm³	ISO 1183
熔流率（熔体流动速率） (300°C/5.0 kg)	14	g/10 min	ISO 1133
收缩率 - 流动方向	0.60	%	ISO 294-4

机械性能	额定值	单位制	测试方法
拉伸应力 (4.00 mm)	60.0	MPa	ISO 527-2
拉伸应变 (断裂, 4.00 mm)	5.0	%	ISO 527-2
弯曲模量 (4.00 mm)	4500	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 1			ISO 180
-20°C	4.0	kJ/m²	ISO 180
23°C	4.0	kJ/m²	ISO 180
无缺口伊佐德冲击强度 2			ISO 180
-20°C	30	kJ/m²	ISO 180
23°C	35	kJ/m²	ISO 180

热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa, 未退火	140	°C	ISO 75-2/Bf
1.8 MPa, 未退火	122	°C	ISO 75-2/Af

电气性能	额定值		测试方法
介电常数 (1.00 GHz)	7.00		内部方法
耗散因数 (1.00 GHz)	6.0E-4		内部方法

注射	额定值	单位制
干燥温度	100 到 120	°C
干燥时间	2.0 到 4.0	hr
加工（熔体）温度	290 到 310	°C
模具温度	80.0 到 110	°C
注射速度	中等偏快