PREPERM® L1000HF
聚苯醚
Premix Oy
产品说明:
PREPERM® L1000HF is a special compound with elevated dielectric constants of 10.
PREPERM® L1000HF is a special compound based on Premix proprietary PPE technology. Ext
PREPERM® L1000HF is a special compound based on Premix proprietary PPE technology. Ext
remely low dissipation factor (< 0.001) makes PREPERM® L1000HF an excellent material for h
igh frequency applications. PREPERM® L1000HF offers stable dielectric constant over wide fre
quency and wide temperature range. PREPERM® L1000HF is modified for injection moulding.
Applications include structural parts for antennas in base stations, point to point, wlan, mobile
Applications include structural parts for antennas in base stations, point to point, wlan, mobile
phones etc. Devices made out of PREPERM® can operate at very high frequencies as PREPERM
® offers stable performance even at 120 GHz.
基本信息 | |
---|---|
特性 |
|
用途 |
|
RoHS 合规性 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 2.32 | g/cm³ | |
熔流率(熔体流动速率) (300°C/5.0 kg) | 8.0 | g/10 min | ISO 1133 |
收缩率 | 0.40 | % | ISO 294-4 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸应力 (4.00 mm) | 45.0 | MPa | ISO 527-2 |
拉伸应变 (断裂, 4.00 mm) | 3.0 | % | ISO 527-2 |
弯曲模量 (4.00 mm) | 6200 | MPa | ISO 178 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
悬壁梁缺口冲击强度 (23°C) | 3.0 | kJ/m² | ISO 180 |
无缺口伊佐德冲击强度 (23°C) | 15 | kJ/m² | ISO 180 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度 | |||
0.45 MPa, 未退火 | 126 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火 | 122 | °C | ISO 75-2/Af |
电气性能 | 额定值 | 测试方法 | |
---|---|---|---|
介电常数 (1.00 GHz) | 10.0 | 内部方法 | |
耗散因数 (1.00 GHz) | 8.0E-4 | 内部方法 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 90.0 到 100 | °C | |
干燥时间 | 2.0 到 4.0 | hr | |
加工(熔体)温度 | 280 到 310 | °C | |
模具温度 | 80.0 到 110 | °C | |
注射速度 | 中等偏快 |