PREPERM® L380 is a special compound with elevated dielectric constants of 3.80.

PREPERM® L380 is based on Premix proprietary PPE technology. Extremely low dissipation fa

ctor (0.0006) makes PREPERM® L380 an excellent material for high frequency applications. PR

EPERM® L380 offers stable dielectric constant over wide frequency and wide temperature rang

e. PREPERM® retains its physical properties at very low (-78°C) temperatures. PREPERM® L380

can be injection moulded or extruded.

Applications include structural parts for antennas in base stations, point to point, wlan, mobile

phones etc. Devices made out of PREPERM® L380 can operate at very high frequencies as PRE

PERM® L380 offers

stable performance even at 120 GHz.

基本信息
特性	低温强度 低温韧性
用途	电气/电子应用领域 电气元件
RoHS 合规性	RoHS 合规
形式	颗粒
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
密度	1.45	g/cm³	ISO 1183
熔流率（熔体流动速率） (300°C/5.0 kg)	12	g/10 min	ISO 1133
收缩率 - 流动方向	1.0	%	ISO 294-4

机械性能	额定值	单位制	测试方法
拉伸应力			ISO 527-2
屈服, 4.00 mm	53.0	MPa	ISO 527-2
4.00 mm	44.0	MPa	ISO 527-2
拉伸应变			ISO 527-2
屈服, 4.00 mm	8.0	%	ISO 527-2
断裂, 4.00 mm	25	%	ISO 527-2
弯曲模量 (4.00 mm)	2200	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 1			ISO 180
-78°C	12	kJ/m²	ISO 180
-20°C	12	kJ/m²	ISO 180
23°C	21	kJ/m²	ISO 180
无缺口伊佐德冲击强度 2			ISO 180
-78°C	无断裂		ISO 180
-20°C	无断裂		ISO 180
23°C	无断裂		ISO 180

热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa, 未退火	178	°C	ISO 75-2/Bf
1.8 MPa, 未退火	155	°C	ISO 75-2/Af

电气性能	额定值		测试方法
介电常数 (1.00 GHz)	3.80		内部方法
耗散因数 (1.00 GHz)	6.0E-4		内部方法

可燃性	额定值		测试方法
UL 阻燃等级 (4.00 mm)	V-1		UL 94

注射	额定值	单位制
干燥温度	120 到 140	°C
干燥时间	2.0 到 4.0	hr
加工（熔体）温度	290 到 310	°C
模具温度	80.0 到 140	°C
注塑压力	60.0 到 80.0	MPa
注射速度	中等

挤出	额定值	单位制
干燥温度	120 到 140	°C
干燥时间	2.0 到 4.0	hr
熔体温度	260 到 280	°C
口模温度	260 到 300	°C