TECANYL®, due to its inherent chemical composition, exhibits unusually low moisture absor

ption. Therefore, good electrical insulating properties are realized over a wide range of humi

dity and temperature conditions. Chemical attack from water, most salt solutions, acids and b

ases is also minimal with TECANYL®. The addition of glass fiber reinforcement enhances both

the mechanical and thermal properties of the basic TECANYL® material. Made from Noryl® E

N265 resin.

Made from Noryl EN265 resin® exhibits a broad range of outstanding properties for applicatio

ns in computers and business equipment, automotive, electrical insulation, telecommunication

s, appliances, electronics, and many other industries.

基本信息
特性	尺寸稳定性良好 低吸湿性 绝缘 抗撞击性，高 水解稳定
用途	电脑组件 电气/电子应用领域 电器用具 绝缘材料 汽车领域的应用 商务设备 通讯器材
形式	Shapes

物理性能	额定值	单位制	测试方法
比重	1.08	g/cm³	ASTM D792
吸水率 (23°C, 24 hr)	0.070	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级, 23°C)	119		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量 (23°C)	2410	MPa	ASTM D638
抗张强度 (断裂, 23°C)	63.4	MPa	ASTM D638
伸长率 (断裂, 23°C)	25	%	ASTM D638
弯曲模量 (23°C)	2550	MPa	ASTM D790
弯曲强度 (23°C)	92.4	MPa	ASTM D790
摩擦系数
与自身 - 动态 1	0.39
与自身 - 静态	0.32

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (23°C)	190	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度			ASTM D648
0.45 MPa, 未退火	137	°C	ASTM D648
1.8 MPa, 未退火	123	°C	ASTM D648
维卡软化温度	154	°C
线形热膨胀系数 - 流动 (-18 到 60°C)	5.9E-5	cm/cm/°C	ASTM D696
最高使用温度
Intermittent	110	°C
Long Term	104	°C

电气性能	额定值	单位制	测试方法
体积电阻率 (23°C)	1.0E+17	ohms·cm	ASTM D257
介电强度	20	kV/mm	ASTM D149
介电常数 2(23°C, 60 Hz)	2.70		ASTM D150
耗散因数 (23°C, 60 Hz)	7.0E-4		ASTM D150

可燃性	额定值	单位制	测试方法
UL 阻燃等级	V-1		UL 94

备注
1 .	40 psi, 50 fpm
2 .	50% RH