3M™ Dyneon™ Fluoroplastic PFA 6502TZ is a fully fluorinated copolymer of TFE & PPVE. The resin has been developed for the transfer molding and extrusion of claddings and linings. The easier processing under low shear rates was one goal and also 3M™ Dyneon™ PFA 6502T Z Fluorothermoplastic was designed to be used in roughest environments, e. g. in the chemical industry, where high strength and extreme thermal and chemical resistance are required.

Features

• Broad processing window

• Improved mold release property

• Improved stress crack resistance

• Smooth surfaces

• High transparency

• Process targets: Transfer molding and extrusion
• 3M™ Dyneon™ Fluoroplastic PFA 6502TZ 物性表

  基本信息
  特性	高强度 共聚物 耐化学性良好 耐热性，高 清晰度，高 脱模性能良好
  用途	衬里
  形式	粒子
  加工方法	吹塑成型 挤出 树脂传递成型 压缩模塑

  物理性能	额定值	单位制	测试方法
  密度	2.15	g/cm³	ISO 12086
  熔流率（熔体流动速率） (372°C/5.0 kg)	2.0	g/10 min	ISO 1133

  硬度	额定值	单位制	测试方法
  肖氏硬度 (邵氏 D)	60		ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸应力 (断裂, 23°C)	30.0	MPa	ISO 527-1
  拉伸应变 (断裂, 23°C)	400	%	ISO 527-1
  弯曲模量	550	MPa	ASTM D790

  热性能	额定值	单位制	测试方法
  熔融温度	310	°C	ISO 12086

  可燃性	额定值	单位制	测试方法
  极限氧指数	> 95	%	ASTM D2863

  挤出	额定值	单位制
  熔体温度	< 400	°C