3M™ Dyneon™ Ultra High Purity PFA 6502UHPZ grades are a new series of ultra-high purity fluorothermoplastics. These resins were developed for high-purity applications requiring ultra-low levels of metal and other cation and anion extractions, such as in the semiconductor market. The 3M™ Dyneon PFA UHPZ family comprises grades that can be compression-molded, transfer-molded, extruded, injection-molded or blow-molded.

Features

• Extremely low level of extractable trace elements

• Extremely low levels of fluoride ions and other anions

• Service temperature range up to 260 °C

• Excellent, almost universal resistance to solvents and chemicals

• UHP packaged to assure clean, contamination-free product
• 3M™ Dyneon™ Fluoroplastic PFA 6502UHPZ 物性表

  基本信息
  特性	Low (to None) Ion Content 纯度高 低萃取物 抗溶剂性 耐化学性良好
  用途	半导体模制化合物
  形式	粒子
  加工方法	吹塑成型 挤出 树脂传递成型 压缩模塑 注射成型

  物理性能	额定值	单位制	测试方法
  密度	2.15	g/cm³	ISO 12086
  熔流率（熔体流动速率） (372°C/5.0 kg)	2.0	g/10 min	ISO 1133

  硬度	额定值	单位制	测试方法
  肖氏硬度 (邵氏 D)	60		ASTM D2240, ISO 868

  机械性能	额定值	单位制	测试方法
  拉伸应力 (断裂, 23°C)	30.0	MPa	ISO 527-1
  拉伸应变 (断裂, 23°C)	330	%	ISO 527-1
  弯曲模量	550	MPa	ASTM D790

  热性能	额定值	单位制	测试方法
  熔融温度	308	°C	ISO 12086

  可燃性	额定值	单位制	测试方法
  极限氧指数	> 95	%	ASTM D2863

  注射	额定值	单位制
  加工（熔体）温度	< 400	°C

  挤出	额定值	单位制
  熔体温度	< 400	°C